Spandex fiber is the abbreviation of polyurethane fiber. The trade names include Lycra (Lycra, the United States, the United Kingdom, the Netherlands, Canada, Brazil), neolon (neolon, Japan), dorlastan (dorlastan, Germany), etc. Firstly, it was successfully studied by German Bayer company in 1937, and American DuPont company began industrial production in 1959. At present, there are nearly 40 factories and seven lines of production, with a total annual output of about 100000 tons, and China's existing production capacity of about 10000 tons. Spandex is a kind of synthetic fiber, which contains more than 85 percent polyurethane.
Postoje dvije varijante spandex vlakana, jedna je mozaični kopolimer aromatske diizocijanaze i poliesterskog segmenta koji sadrži hidroksil (u daljnjem tekstu poliesterski spandex), a drugi je mozaični kopolimer aromatskog diizocijanata i polieterskog segmenta koji sadrži hidroksil polieterski spandex). Spandex vlakna, elastična poliolefinska vlakna i elastična kompozitna vlakna zajednički se nazivaju elastičnim vlaknima.
Sintetičko vlakno s visokim rastezanjem pri prekidu (više od 400 posto), niskim modulom i visokim elastičnim povratom. Kineski trgovački naziv višeblok poliuretanskih vlakana. Također poznato kao elastična vlakna. Spandex ima visoko rastezanje (500 posto 700 posto), nizak modul elastičnosti (200 posto istezanje, 0,04 0,12 g / dan) i visoku elastičnost (200 posto istezanje, 95 posto 99 posto). Osim visoke čvrstoće, ostala fizikalna i mehanička svojstva vrlo su slična prirodnoj svili od lateksa. Otpornija je na kemijsku degradaciju od žice od lateksa, ima srednju toplinsku stabilnost, a temperatura omekšavanja je iznad 200 stupnjeva. Većina bojila i završnih sredstava koja se koriste za sintetička i prirodna vlakna također su prikladna za bojenje i završnu obradu spandeksa. Spandex je otporan na znoj, morsku vodu i na razna kemijska sredstva za čišćenje i većinu krema za sunčanje. Dugotrajno izlaganje sunčevoj svjetlosti ili izbjeljivaču s klorom također će izblijedjeti, ali stupanj blijeđenja uvelike varira ovisno o vrsti spandexa.
Spandex fiber has such high elasticity because its polymer chain is composed of low melting point and amorphous "soft" segments as the matrix and high melting point and crystalline "hard" segments embedded in it. Flexible chain segments form a certain network structure by certain cross{{0}}linking between molecular chains. Due to the small interaction force between molecular chains, they can stretch freely, resulting in large elongation. The molecular linkage force of rigid segment is relatively large, and the molecular chain will not elongate indefinitely, resulting in high resilience. Most of the cross sections of radon fiber filaments are dog bone shaped, and some filaments have smooth or serrated surfaces. The breaking strength is the lowest among all textile fibers, only 0.44 0.88cn/dtex (the strength of polyether type is higher than that of polyester type). The moisture absorption range is small, generally 0.3-1.2 percent (the moisture absorption rate of multifilament is slightly higher than that of monofilament). The heat resistance varies greatly depending on the variety. Most fibers are stored in the range of 90 150 degree for a short time, and the fibers will not be damaged. The safe ironing temperature is below 150 degree , which can be heated and wet washed. It has excellent dyeing performance and can be dyed into various colors. The dyes have strong affinity for fiber, can adapt to most kinds of dyes, and has good chemical resistance, resistance to most acid and alkali, chemicals, organic solvents, dry cleaners and bleaches, as well as resistance to sunlight and wind and snow, but not oxide, which is easy to turn yellow and reduce the strength of fiber.
Spandex se općenito ne koristi sam, već se mala količina umiješa u tkaninu. Ova vrsta vlakana ima svojstva gume i vlakana. Većina ih se koristi u pređi s jezgrom sa spandexom kao središnjom pređom, koja se naziva elastična predena pređa s jezgrom. Glavne karakteristike ove pređe su sljedeće: prvo, može postići dobar osjećaj i izgled u ruci, a vanjska vlakna sastavljena od prirodnih vlakana dobro upijaju vlagu; Drugo, samo 1-10 posto spandex filamenta može proizvesti visokokvalitetnu elastičnu pređu; Treće, kontrolni raspon postotka elastičnosti je od 10 posto do 20 posto, a različite elastične vrijednosti mogu se odabrati prema namjeni proizvoda. Lako se vrti svila od 25 2500 denijera različite debljine, pa se naširoko koristi za izradu elastičnih tkanih tkanina, kao što su čarape, pokrivači za namještaj, skijaška odjeća, sportska odjeća, medicinske tkanine, pojasevi, intendantska oprema, elastični dijelovi zrakoplovstva odjeća, itd. Kako ljudi postavljaju nove zahtjeve za tkanine, kao što su lagana težina, udobno pristajanje i mekana tekstura, udio tkanina od spandeksa niskog denijera u tkaninama od sintetičkih vlakana također se povećava. Također se koristi kao upredena pređa nastala kombinacijom gole svile od spandeksa i spandexa i drugih vlakana. Uglavnom se koristi za sve vrste pletenih i potkovanih pletenih tkanina, tkanih tkanina i elastičnih tkanina.